Dissertação

{pt_PT=Separation of ABS and PS plastics from waste electrical and electronic equipment with froth flotation using a physical conditioning technique} {} EVALUATED

{pt=Este trabalho propõe a utilização de uma metodologia experimental que envolve a utilização da flutuação por espumas combinada com um condicionamento físico para separar ABS e PS provenientes de resíduos de equipamentos eléctricos e electrónicos. Foi desenvolvido um arranjo de experiências ortogonal L16 de dois níveis usando a metodologia de Taguchi com 7 variáveis manipuladas: tempo e temperatura do tratamento, tempo decorrido entre o final do tratamento e a flutuação, concentração de espumante (MIBC), caudal de ar, velocidade do rotor e pH. Usando o tratamento proposto, foi possível obter uma recuperação média de ABS no produto flutuado de 98% e a recuperação do PS variou entre 3 e 55%, indicando que nas condições de tratamento foi possível deprimir o PS, praticamente mantendo a flutuabilidade de ABS. Foi possível obter um modelo linear (R^2=0,8852) para explicar a resposta do Índice de Selectividade e foi demonstrado que a velocidade do rotor e as interacções entre concentração de espumante e tempo decorrido, e o caudal de ar e o pH têm maior influência no processo. A grande variabilidade de resultados pautou o trabalho experimental. Foram realizadas análises suplementares para estudar a adequabilidade da metodologia proposta para produzir materiais de qualidade para a indústria de reciclagem, bem como revelar os mecanismos de actuação do tratamento. Os resultados obtidos mostram a capacidade do tratamento proposto em separar o ABS do PS e a sua possível aplicação na indústria da reciclagem. , en=This work focuses on the separation of ABS and PS plastics from waste of electrical and electronic equipment using froth flotation combined with a physical conditioning technique. A two-level L16 Orthogonal Array of Experiments using the Taguchi design of experiences approach was developed with 7 manipulated variables: treatment time; treatment temperature and elapsed time between the end of the heating treatment and the flotation test, frother (MIBC) concentration, air flow rate, impeller speed and pH. The tests were performed on PS and ABS with size ranging from 2 to 4 mm. Using the heating treatment it was obtained an average ABS recovery in the floated product of 98% was and the PS recovery ranged from 3 to 55% indicating that under the treatment conditions PS was depressed while the overall floatability of ABS was slightly altered. A linear model (R^2 coefficient of 0,8852) was found to explain the Selectivity Index response and it was demonstrated that impeller speed and interaction between frother concentration and elapsed time, and air flow rate and pH have the most influence on the process efficiency. Data variability and results have characterized the experimental work. Supplementary analysis was carried out to evaluate the adequacy of the proposed separation method for the plastic recycling industry. The results show that the proposed treatment can separate PS from ABS, and their possible application in the recycling industry, as well as to disclose the mechanism of action of the treatment. }
{pt=Separação de plásticos, REEE, flutuação por espumas, Método de Taguchi, ABS, PS, en=Plastics separation, WEEE plastics, froth flotation, Taguchi design of experiments, ABS, PS}

Junho 26, 2019, 11:0

Orientação

ORIENTADOR

Maria Teresa Da Cruz Carvalho

Departamento de Engenharia Civil, Arquitectura e Georrecursos (DECivil)

Professor Associado